Search found 94 matches
- Wed Apr 18, 2018 6:57 pm
- Forum: Resins
- Topic: SolusCast: Cracks in heavy model
- Replies: 116
- Views: 160644
Re: SolusCast: Cracks in heavy model
Hello, I have DVP Italy LC12 ( DVP 12m3) vacuum pump....after putting in flask will upload image so everybody can see...if need changes i'll do then after will cast..... I use silver sprue which was cast(tree parts)....i don't mix silver dust/powder...also I get too much holes while cut spure ends n...
- Mon Apr 16, 2018 7:11 pm
- Forum: Resins
- Topic: SolusCast: Cracks in heavy model
- Replies: 116
- Views: 160644
Re: SolusCast: Cracks in heavy model
Hi, will try again SC resin same door after putting in flasks will share you image if need to change will do then cast... @ Jewelermdt what do you mean by feeds (vibrating after pouring investment?).....tilted also i didn't understand can u give some picture.... cast burn out will do as per said ben...
- Sun Apr 15, 2018 4:07 pm
- Forum: Resins
- Topic: SolusCast: Cracks in heavy model
- Replies: 116
- Views: 160644
Re: SolusCast: Cracks in heavy model
what i did as said early nothing to hid, door details is more important! (after print cleaning in warm soap water by using Ultrasonic, curing unit from Reify, curing already done 8 hours under water, remove supports again curing underwater 3hr & without water 2 hours). 40/100 with boric powder 2...
- Sat Apr 14, 2018 7:11 pm
- Forum: Resins
- Topic: SolusCast: Cracks in heavy model
- Replies: 116
- Views: 160644
Re: SolusCast: Cracks in heavy model
@ mongerdesigns- SRS cadcast investment.
- Sat Apr 14, 2018 4:46 pm
- Forum: Resins
- Topic: SolusCast: Cracks in heavy model
- Replies: 116
- Views: 160644
Re: SolusCast: Cracks in heavy model
images below
- Sat Apr 14, 2018 4:40 pm
- Forum: Resins
- Topic: SolusCast: Cracks in heavy model
- Replies: 116
- Views: 160644
Re: SolusCast: Cracks in heavy model
More images below
- Sat Apr 14, 2018 4:34 pm
- Forum: Resins
- Topic: SolusCast: Cracks in heavy model
- Replies: 116
- Views: 160644
Re: SolusCast: Cracks in heavy model
Hello Everyone, Sorry for delay....@M-Williams thank you i used cool water and will continue, check below images....i'm not 100% happy with casting special for door details what could be the problem?... @ 775C 5 hours did vacuum flasks for almost 1 min then return in oven after 2 1/2 hours did casti...
- Thu Mar 29, 2018 4:11 pm
- Forum: Resins
- Topic: SolusCast: Cracks in heavy model
- Replies: 116
- Views: 160644
Re: SolusCast: Cracks in heavy model
Hello Everyone, I.m going to try casting SC & b9 emerald resin, print of SC came out detailing..... After print cleaning in warm soap water by using Ultrasonic, curing unit from Reify, curing already done 8 hours under water, remove supports again curing underwater 3hr & without water 2 hour...
- Tue Feb 13, 2018 7:11 pm
- Forum: Casting
- Topic: Casting SolusCast
- Replies: 202
- Views: 299956
Re: Casting SolusCast
Hello Everyone, I did casting 18kt White gold using b9 emerald n small loops (SC resin) curving 10 hours underwater UV nail box n 2 hours normal oven @75° C.....CADCAST SRS 40/100 investment 5 hours bench then 150° C for 2 hours, 465°C 1 hour, 775°C 7 hours, vacuum flask abt 20 seconds, casting @630...
Re: 1.9.4v
first i did 10 10 10 all then i print 6x4x2 almost like in video but i did not change original scale that is why platform area small....after i enter 6 x 4 x 10 at original scale and actual scale 5.98x 4.02 x 10 platform correct.. now again i'm printing 6x4x2 to see as per video doing....is it right.