My second print is a very heavy class ring and after curing, I noticed cracks in the ring. I figured I left it in the alcohol rinse too long or maybe it was just a fluke, so I reprinted it.
The second print is actually a little worse and the cracks are in different spots.
Looking at it through my microscope, I saw that the build lines get a little more noticeable right before the cracks. Might be a film issue? Too little/not enough exposure? I used the new fangled spacer thing when I installed this film right before I first used the SolusCast.
Maybe they are small enough that they won't be an issue? I mean, I have to use magnification to see them.
Thanks in advance for any insight. I got the best picture I could through the scope. Photography is not my strongest skill, lol.